Introduction: LEXAN EXL1330 polycarbonate (PC) siloxane copolymer resin is a UV stabilized opaque injection molding (IM) and sheet extrusion grade. This resin offers extreme low temperature (-60 C) ductility in combination with medium flow characteristics and excellent processability with opportunities for shorter IM cycle times compared to standard PC. LEXAN EXL1330 resin is a general purpose product available in a wide range of opaque colors and is an excellent candidate for a broad range of application .

Introduction: Mobile phone back panels, new energy vehicle charging piles, car charging gun casings, photovoltaic connectors, 5G base station casings, explosion-proof shields, helmets, gun butts, radar antennas, etc.

Free Sample
Inquiry Now

제품 기능

01
사출 성형 학년, 압출 학년, 플레이트 학년
02
Anti-UV 학년;
03
중간 유동성;
04
낮은 온도에서 높은 연성;
05
짧은 성형 cycle.

제품 매개 변수

검사 항목	표준	단위	값	/
밀도	희박 가 D792	g/cm ³	1.18
수축 흐름 3.2mm	내부 방법	%	0.4-0.8
물 흡수 23℃ 포화	ISO 62	%	35
물 흡수 23℃ 50RH	ISO 62	%	0. 15
지수 300℃ 1.2kg를 녹입니다	희박 가 D1238	g/니다	10
야외 적합성을	UL 746C	/	f1
볼 움푹 들어간 경도 H358/30	ISO 2039	Mpa	90
인장 모듈러스 50mm/min	희박 가 D638	MPa	2100
인장 강도 항복 50mm/min Typel	희박 가 D638	MPa	58
인장 강도 파단 50mm/min Typel	희박 가 D638	Mpa	61
신장 수율 50mm/min Typel	희박 가 D638	%	6
Elongation Break 50mm/min Typel	희박 가 D638	%	130
휨강도 항복 1.3mm/min	희박 가 D790	Mpa	88
휨탄성률 1.3mm/min	희박 가 D790	Mpa	2060
아이조드 노치 충격 23℃	희박 가 D256	J/m	801
아이조드 노치 충격-30℃	희박 가 D256	J/m	680
아이조드 노치 충격-50℃	희박 가 D256	J/m	587
아이조드 노치 충격 23℃ 6.4mm	희박 가 D256	J/m	640
아이조드 노치 충격 23℃ 이중화	내부 방법	J/m	1068
타 보르는 CS-17 휠 1kg 착용	내부 방법	mg/1000cy	10
계측된 영향 23℃ 총 에너지	희박 가 D3763	J	52
HDT 풀림 0.45Mpa 3.2mm	희박 가 D648	℃	134
HDT Unannealed 1.8Mpa 3.2mm	희박 가 D648	℃	120
HDT Unannealed 1.8Mpa 6.4mm	희박 가 D648	℃	124
Vicat 50℃/hr 50N	희박 가 D1525	℃	143
CLE Flow-40.0-40℃	희박 가 E831	cm/cm/℃	6.66E-5
CLE xFlow-40.0-40℃	희박 가 E831	cm/cm/℃	6.66E-5