PC EXL1192T

Introduction: Lexan EXL1192T polycarbonate (PC) siloxane copolymer resin is a transparent injection molding (IM) grade with extra release properties for food contact applications. This resin offers good low temperature (-20 C) ductility in combination with high flow characteristics and excellent processability with opportunities for shorter IM cycle times compared to standard PC resins. Lexan EXL1192T resin offers enhanced release performance, is available in transparent colors and is an excellent candidate for a broad range of applications in food handling or food preparation markets.

Introduction: food contact applications.Outdoor Products.

Free Sample
Inquiry Now

제품 기능

01
높은 흐름이다.
02
낮은 온도에서 높은 연성.
03
좋은 Mould 릴리스.
04
좋은 processability이다.
05
다양한 응용이 가능합니다.

제품 매개 변수

검사 항목	표준	단위	값	/
밀도	희박 가 D792	g/cm ³	1. 19명
수축 흐름 3.2mm	내부 방법	%	0.4-0.8
물 흡수 23℃ 포화	ISO 62	%	밝 혔
물 흡수 23℃ 50RH	ISO 62	%	0. 09
지수 300℃ 1.2kg를 녹입니다	희박 가 D1238	g/니다	20
록웰 HardnesL (규모)	희박 가 D785	/	89
인장 모듈러스 50mm/min	희박 가 D638	MPa	2260
인장 강도 항복 50mm/min Typel	희박 가 D638	MPa	58
인장 강도 파단 50mm/min Typel	희박 가 D638	MPa	57
신장 수율 50mm/min	희박 가 D638	%	5. 7
Elongation 브레이크 50mm/min	희박 가 D638	%	117.9
휨강도 항복 1.3mm/min	희박 가 D790	Mpa	94
휨탄성률 1.3mm/min	희박 가 D790	Mpa	2240
아이조드 노치 충격 23℃	희박 가 D256	J/m	736
아이조드 노치 충격-30℃	희박 가 D256	J/m	618
Charpy 노치 충격 23℃ 1eA	ISO 179	KJ/m ²	65
Charpy 노치 충격-30℃ 3.0mm 1eA	ISO 179	KJ/m ²	45
계측된 영향 23℃ 총 에너지	희박 가 D3763	J	74
투과 율	희박 가 D1003	%	82
안개	희박 가 D1003	%	3
HDT Unannealed 1.8Mpa 3.2mm	희박 가 D648	℃	121
HDT 1.8MPa 4.0mm이다	ISO 75	℃	116
Vicat 50℃/hr 10N	희박 가 D1525	℃	138
Vicat 50℃/hr 50N	ISO 306	℃	138
Vicat 120℃/hr 50N	ISO 306	℃	139